LNP LUBRICOMP RBL36XXJ compound is based on Nylon 6/6 resin containing 30% glass bead, 15% PTFE. Added features of this grade include: Low Extractable, Healthcare, Wear Resistant, Food Contact compliant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 435 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 51 | J/m | ASTM D256 |
| Multiaxial Impact | 1 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy, 23°C | 5 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 27 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 280 - 305 | °C | |
| Front - Zone 3 Temperature | 295 - 305 | °C | |
| Middle - Zone 2 Temperature | 280 - 295 | °C | |
| Rear - Zone 1 Temperature | 265 - 275 | °C | |
| Mold Temperature | 95 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 64 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 8.5 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 10 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 3990 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3740 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 64 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 8.3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3930 | MPa | ISO 527 |
| Flexural Stress | 107 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3560 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.49 | - | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.41 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 2 - 4 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 1 - 3 | % | ASTM D955 |
| Wear Factor Washer | 41 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Wear Factor Ring | 8 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.47 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.44 | - | ASTM D3702 Modified: Manual |
| Density | 1.49 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.58 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 236 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 83 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 6.90E-05 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 8.30E-05 | 1/°C | ASTM D696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 203 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 73 | °C | ISO 75/Af |