LNP LUBRICOMP RFL36 compound is based on Nylon 6/6 resin containing 30% glass fiber, 15% PTFE. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*3 -40°C | 12 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 84 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -40°C | 74 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 16 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 280 - 305 | °C | |
| Front - Zone 3 Temperature | 295 - 305 | °C | |
| Middle - Zone 2 Temperature | 280 - 295 | °C | |
| Rear - Zone 1 Temperature | 265 - 275 | °C | |
| Mold Temperature | 95 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 166 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.6 | % | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 234 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 277 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 4.1 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 9100 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min, 60°C | 6.1 | % | ISO 178 |
| Flexural Strain, break, 2 mm/min, 100°C | 6.6 | % | ISO 178 |
| Flexural Strain, break, 2 mm/min, 150°C | 5.6 | % | ISO 178 |
| Flexural Strain, break, 2 mm/min, 200°C | 6.3 | % | ISO 178 |
| Flexural Stress, yield, 2 mm/min, 60°C | 179 | MPa | ISO 178 |
| Flexural Stress, yield, 2 mm/min, 100°C | 131 | MPa | ISO 178 |
| Flexural Stress, yield, 2 mm/min, 150°C | 96 | MPa | ISO 178 |
| Flexural Stress, yield, 2 mm/min, 200°C | 83 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min, 60°C | 5300 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min, 100°C | 4200 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min, 150°C | 3500 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min, 200°C | 3100 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Wear Factor Washer | 12 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.59 | - | ASTM D3702 Modified: Manual |
| Density | 1.51 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/24hrs) | 1.34 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.46 | % | ISO 62 |
| Melt Volume Rate, MVR at 275°C/5 kg | 15 - 20 | cm³/10 min | ISO 1133 |
| Mold Shrinkage, flow, 24 hrs | 0.2 - 0.5 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.8 - 1.2 | % | ISO 294 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Heat | 1988 | J/kg-K | ASTM E1269 |
| CTE, 23°C to 60°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 7.5E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | >220 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | >220 | °C | ISO 75/Af |
| Thermal Conductivity | 0.25 | W/m-K | ASTM D5930 |
| Relative Temp Index, Elec | 120 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.