LNP LUBRICOMP RFL36S compound is based on Nylon 6/6 resin containing 30% glass fiber, 15% PTFE. Added features of this grade include: Wear Resistant, Heat Stabilized.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 100 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 1040 | J/m | ASTM D4812 |
| Instrumented Dart Impact Energy @ peak, 23°C | 10 | J | ASTM D3763 |
| Izod Impact, notched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 70 | kJ/m² | ISO 180/1U |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 16 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 85 | kJ/m² | ISO 179/1eU |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 280 - 305 | °C | |
| Rear - Zone 1 Temperature | 265 - 275 | °C | |
| Middle - Zone 2 Temperature | 280 - 295 | °C | |
| Front - Zone 3 Temperature | 295 - 305 | °C | |
| Mold Temperature | 95 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Modulus, 5 mm/min | 10350 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 150 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 8300 | MPa | ASTM D790 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 240 | MPa | ASTM D790 |
| Tensile Modulus, 1 mm/min | 10300 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3.2 | % | ISO 527 |
| Tensile Stress, break, 5 mm/min | 160 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/min | 8900 | MPa | ISO 178 |
| Flexural Strength, 2 mm/min | 235 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.5 | g/cm³ | ASTM D792 |
| Water Absorption, (23°C/24hrs) | 0.5 - 1 | % | ASTM D570 |
| Melt Flow Rate, 300°C/2.16 kgf | 23 | g/10 min | ASTM D1238 |
| Dynamic COF | 0.57 | - | ASTM D3702 Modified: Manual |
| Wear Factor Washer | 16 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Static COF | 0.46 | - | ASTM D3702 Modified: Manual |
| Density | 1.5 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/24hrs) | 0.5 - 1 | % | ISO 62-1 |
| Melt Volume Rate, MVR at 300°C/2.16 kg | 22 | cm³/10 min | ISO 1133 |
| Mold Shrinkage, flow | 0.2 - 0.5 | % | SABIC method |
| Mold Shrinkage, xflow | 0.8 - 1.2 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 254 | °C | ASTM D648 |
| Vicat Softening Temp, Rate B/50 | 253 | °C | ASTM D1525 |
| CTE, -40°C to 40°C, flow | 3.8E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 5.5E-05 | 1/°C | ASTM E831 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 248 | °C | ISO 75/Af |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 260 | °C | ISO 75/Bf |
| Vicat Softening Temp, Rate B/120 | 250 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 253 | °C | ISO 306 |
| CTE, 23°C to 60°C, flow | 2.8E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 8.3E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, flow | 3.8E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 5.5E-05 | 1/°C | ISO 11359-2 |