LNP LUBRICOMP RFL46 compound is based on Nylon 6/6 resin containing 30% glass fiber, 20% PTFE. Added features of this grade include: Wear Resistant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 66 (Nylon 66)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High stiffness/Strength
Wear resistant

Industry

Material previously used in

Building Component
Commercial Appliance
Electrical
Home Appliances
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	9	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	50	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	8	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	45	kJ/m²	ISO 179/1eU
Izod Impact, notched, 23°C	80	J/m	ASTM D256
Izod Impact, unnotched, 23°C	760	J/m	ASTM D4812

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	280 - 305	°C
Front - Zone 3 Temperature	295 - 305	°C
Middle - Zone 2 Temperature	280 - 295	°C
Rear - Zone 1 Temperature	265 - 275	°C
Mold Temperature	95 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break, 5 mm/min	145	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.5	%	ISO 527
Tensile Modulus, 1 mm/min	10400	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	213	MPa	ISO 178
Flexural Modulus, 2 mm/min	8700	MPa	ISO 178
Flexural Modulus, 1.3 mm/min, 50 mm span	8400	MPa	ASTM D790
Flexural Strength, 1.3 mm/min, 50 mm span	204	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.54	g/cm³	ISO 1183
Moisture Absorption, (23°C/50% RH/24hrs)	0.1 - 0.3	%	ISO 62-4
Moisture Absorption, (23°C/50% RH/Equilibrium)	0.4 - 0.6	%	ISO 62-4
Water Absorption, (23°C/24hrs)	0.7 - 0.9	%	ISO 62-1
Water Absorption, (23°C/saturated)	3.8 - 4.1	%	ISO 62-1
Mold Shrinkage, flow	0.3 - 0.5	%	SABIC method
Mold Shrinkage, xflow	1.0 - 1.4	%	SABIC method
Specific Gravity	1.54	-	ASTM D792
Dynamic COF	0.59	-	ASTM D3702 Modified: Manual
Static COF	0.9	-	ASTM D3702 Modified: Manual
Wear Factor Washer	16	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	253	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	262	°C	ISO 75/Af
Vicat Softening Temp, Rate B/120	251	°C	ISO 306
Vicat Softening Temp, Rate A/50	254	°C	ISO 306
CTE, 23°C to 60°C, flow	2.40E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	9.00E-05	1/°C	ISO 11359-2
HDT, 0.45 MPa, 3.2 mm, unannealed	262	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	254	°C	ASTM D648

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES