IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
LNP LUBRICOMP RKN14 compound is based on Nylon 6/6 resin containing 20% mineral and Molybdenum diSulfide (MoS2). Added features of this grade include: Dimensional Control, Wear Resistant
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.15 - 0.25 | % | |
Melt Temperature | 275 - 290 | °C | |
Front - Zone 3 Temperature | 295 - 305 | °C | |
Middle - Zone 2 Temperature | 280 - 295 | °C | |
Rear - Zone 1 Temperature | 265 - 275 | °C | |
Mold Temperature | 80 - 95 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break, 5 mm/min | 77 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 4.2 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 6300 | MPa | ISO 527 |
Flexural Stress, break, 2 mm/min | 111 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 5000 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage on Tensile Bar, flow | 0.7 - 0.9 | % | SABIC method |
Density | 1.34 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 104 | °C | ISO 75/Af |