FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
LNP LUBRICOMP RL003 compound is based on Nylon 6/6 resin containing 15% PTFE. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 1014 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 32 | J/m | ASTM D256 |
Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.15 - 0.25 | % | |
Melt Temperature | 275 - 290 | °C | |
Front - Zone 3 Temperature | 295 - 305 | °C | |
Middle - Zone 2 Temperature | 280 - 295 | °C | |
Rear - Zone 1 Temperature | 265 - 275 | °C | |
Mold Temperature | 80 - 95 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 73 | MPa | ASTM D638 |
Tensile Strain, break | 11 | % | ASTM D638 |
Flexural Stress | 103 | MPa | ASTM D790 |
Tensile Stress, break | 73 | MPa | ISO 527 |
Tensile Strain, break | 8.9 | % | ISO 527 |
Flexural Stress | 90 | MPa | ISO 178 |
Flexural Modulus | 2900 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.23 | g/cm³ | ASTM D792 |
Mold Shrinkage, xflow, 24 hrs | 1 - 3 | % | ASTM D955 |
Mold Shrinkage, flow, 24 hrs | 1 - 3 | % | ISO 294 |
Wear Factor Washer | 28 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Dynamic COF | 0.32 | - | ASTM D3702 Modified: Manual |
Static COF | 0.3 | - | ASTM D3702 Modified: Manual |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 82 | °C | ISO 75/Af |
Relative Temp Index, Elec | 65 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.15 - 0.25 | % | |
Melt Temperature | 275 - 290 | °C | |
Front - Zone 3 Temperature | 295 - 305 | °C | |
Middle - Zone 2 Temperature | 280 - 295 | °C | |
Rear - Zone 1 Temperature | 265 - 275 | °C | |
Mold Temperature | 80 - 95 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break, 5 mm/min | 59 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 7 | % | ISO 527 |
Flexural Stress, break, 2 mm/min | 83 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.23 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
CTE, 23°C to 60°C, flow | 1.11E-04 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 1.15E-04 | 1/°C | ISO 11359-2 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 82 | °C | ISO 75/Af |
Relative Temp Index, Elec | 65 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |