LNP LUBRICOMP RL0039XP compound is based on Nylon 6/6 resin containing 15% PTFE. Added features of this grade include: Flame Retardant, Internally Lubricated, Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Compliant, 94V-0 Flame Class Rating | 3 | mm | UL 94 by SABIC-IP |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 3 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 275 - 290 | °C | |
| Front - Zone 3 Temperature | 295 - 305 | °C | |
| Middle - Zone 2 Temperature | 280 - 295 | °C | |
| Rear - Zone 1 Temperature | 265 - 275 | °C | |
| Mold Temperature | 80 - 95 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 51 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3100 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 83 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 82 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 4.5 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 2700 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage, flow | 1.3 | % | SABIC method |
| Density | 1.44 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 7.3E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 149 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 89 | °C | ISO 75/Af |