LNP™ LUBRICOMP™ Compound RX18020

LNP™ LUBRICOMP™ RX18020 is a compound based on PA 66 resin containing Glass Fiber, Proprietary Lubricant. Added features include; Internally Lubricated,

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 66 (Nylon 66)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Europe

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High stiffness/Strength
No PFAS intentionally added
Wear resistant

Industry

Material previously used in

Applications

Possible usage of material

Structure

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Glow Wire Ignitability Temperature, 1.5 mm	700	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 1.0 mm	700	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 0.8 mm	700	°C	IEC 60695-2-13
Glow Wire Flammability Index, 1.5 mm	675	°C	IEC 60695-2-12
Glow Wire Flammability Index, 1.0 mm	675	°C	IEC 60695-2-12
Glow Wire Flammability Index, 0.8 mm	675	°C	IEC 60695-2-12

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	8	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	53	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	8	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	65	kJ/m²	ISO 179/1eU
Izod Impact, notched, 23°C	60	J/m	ASTM D256
Izod Impact, unnotched, 23°C	757	J/m	ASTM D4812

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	95 - 100	°C
Drying Time	6 - 8	Hrs
Drying Time (Cumulative)	12	Hrs
Melt Temperature	250 - 280	°C
Rear - Zone 1 Temperature	240 - 260	°C
Middle - Zone 2 Temperature	250 - 270	°C
Front - Zone 3 Temperature	260 - 280	°C
Nozzle Temperature	255 - 275	°C
Mold Temperature	60 - 90	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	60 - 100	rpm
Vent Depth	0.025 - 0.076	mm
Shot to Cylinder Size	40 - 60	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 1 mm/min	6100	MPa	ISO 527
Tensile Stress, break, 5 mm/min	121	MPa	ISO 527
Tensile Strain, break, 5 mm/min	4	%	ISO 527
Flexural Modulus, 2 mm/min	4800	MPa	ISO 178
Flexural Strength, 2 mm/min	174	MPa	ISO 178
Tensile Modulus, 5 mm/min	6200	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	118	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	4	%	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	4600	MPa	ASTM D790
Flexural Strength, 1.3 mm/min, 50 mm span	160	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.21	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.2 - 0.4	%	ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg	69	cm³/10 min	ISO 1133
Specific Gravity	1.21	-	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.1 - 0.2	%	ASTM D570
Wear Factor Washer	8	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF	0.34	-	ASTM D3702 Modified: Manual
Static COF	0.51	-	ASTM D3702 Modified: Manual
Mold Shrinkage, flow	0.5 - 0.7	%	SABIC method
Mold Shrinkage, xflow	1.1 - 1.3	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	231	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	255	°C	ISO 75/Bf
Vicat Softening Temp, Rate B/50	244	°C	ISO 306
Vicat Softening Temp, Rate B/120	246	°C	ISO 306
CTE, 23°C to 60°C, flow	3.8E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	9.6E-05	1/°C	ISO 11359-2
HDT, 1.82 MPa, 3.2mm, unannealed	247	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	257	°C	ASTM D648

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES