LNP LUBRICOMP SCL36 compound is based on Nylon 12 resin containing 15% PTFE, 30% carbon fiber. Added features of this grade include: Wear Resistant, Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 686 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 129 | J/m | ASTM D256 |
| Multiaxial Impact | 4 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy, 23°C | 14 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 39 | kJ/m² | ISO 180/1U |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.12 - 0.2 | % | |
| Melt Temperature | 225 - 240 | °C | |
| Front - Zone 3 Temperature | 225 - 240 | °C | |
| Middle - Zone 2 Temperature | 220 - 230 | °C | |
| Rear - Zone 1 Temperature | 215 - 225 | °C | |
| Mold Temperature | 70 - 80 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 157 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.9 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 21400 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 215 | MPa | ASTM D790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 214 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 15800 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 130 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 19420 | MPa | ISO 527 |
| Flexural Stress | 206 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 16490 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.3 | - | ASTM D792 |
| Density | 1.3 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.09 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.3 - 0.5 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 - 0.6 | % | ASTM D955 |
| Wear Factor Washer | 22 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Wear Factor Ring | 0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.41 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.3 | - | ASTM D3702 Modified: Manual |
| Moisture Absorption (23°C / 50% RH) | 0.14 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 178 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 173 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 2.9E-05 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 6.3E-05 | 1/°C | ASTM D696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 177 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 170 | °C | ISO 75/Af |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 694 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 117 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 124 | MPa | ASTM D638 |
| Tensile Strain, break | 2.7 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 15720 | MPa | ASTM D638 |
| Flexural Stress | 206 | MPa | ASTM D790 |
| Flexural Modulus | 13850 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 168 | °C | ASTM D648 |