FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
LNP LUBRICOMP SCP36 compound is based on Nylon 12 resin containing 30% carbon fiber, 15% PTFE/silicone. Added features of this grade include: Wear Resistant, Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 508 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 82 | J/m | ASTM D256 |
Multiaxial Impact | 2 | J | ISO 6603 |
Instrumented Dart Impact Total Energy, 23°C | 10 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*4 +23°C | 34 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 100 - 105 | °C | |
Drying Time | 3 - 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 260 - 280 | °C | |
Nozzle Temperature | 250 - 270 | °C | |
Front - Zone 3 Temperature | 260 - 280 | °C | |
Middle - Zone 2 Temperature | 250 - 270 | °C | |
Rear - Zone 1 Temperature | 240 - 260 | °C | |
Hopper Temperature | 40 - 60 | °C | |
Mold Temperature | 60 - 85 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Flexural Stress, brk, 1.3 mm/min, 50 mm span | 178 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 16200 | MPa | ASTM D790 |
Tensile Stress, break, 5 mm/min | 122 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 1 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 18160 | MPa | ISO 527 |
Flexural Modulus, 2 mm/min | 16030 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.26 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.16 | % | ASTM D570 |
Mold Shrinkage, flow, 24 hrs | 0.1 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.5 | % | ASTM D955 |
Wear Factor Washer | 14 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Wear Factor Ring | 0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Dynamic COF | 0.47 | - | ASTM D3702 Modified: Manual |
Static COF | 0.33 | - | ASTM D3702 Modified: Manual |
Moisture Absorption (23°C / 50% RH) | 0.24 | % | ISO 62 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 178 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 173 | °C | ASTM D648 |
CTE, -30°C to 30°C, flow | 3.2E-05 | 1/°C | ASTM D696 |
CTE, -30°C to 30°C, xflow | 4.1E-05 | 1/°C | ASTM D696 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 177 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 169 | °C | ISO 75/Af |
Relative Temp Index, Elec | 65 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |