IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 907 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 112 | J/m | ASTM D256 |
LNP LUBRICOMP SFL2A compound is based on Nylon 12 resin containing 50% glass fiber, 10% PTFE. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 907 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 112 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.12 - 0.2 | % | |
Melt Temperature | 225 - 240 | °C | |
Front - Zone 3 Temperature | 225 - 240 | °C | |
Middle - Zone 2 Temperature | 220 - 230 | °C | |
Rear - Zone 1 Temperature | 215 - 225 | °C | |
Mold Temperature | 70 - 80 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 149 | MPa | ASTM D638 |
Tensile Strain, break | 3.5 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 16060 | MPa | ASTM D638 |
Flexural Stress | 241 | MPa | ASTM D790 |
Flexural Modulus | 13120 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.64 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.6 | % | ASTM D570 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 174 | °C | ASTM D648 |