FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 0.75 | mm | UL 94 |
LNP LUBRICOMP SFL36 compound is based on Nylon 12 resin containing 30% glass fiber, 15% PTFE. Added features of this grade include: Internally Lubricated, Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 0.75 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 65 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.12 - 0.2 | % | |
Melt Temperature | 225 - 240 | °C | |
Front - Zone 3 Temperature | 225 - 240 | °C | |
Middle - Zone 2 Temperature | 220 - 230 | °C | |
Rear - Zone 1 Temperature | 215 - 225 | °C | |
Mold Temperature | 70 - 80 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield, 5 mm/min | 100 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 4.5 | % | ISO 527 |
Flexural Stress, yield, 2 mm/min | 147 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 5900 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage, flow | 0.1 - 0.3 | % | SABIC method |
Density | 1.37 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/24hrs) | 0.14 | % | ISO 62-1 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
CTE, 23°C to 60°C, flow | 2.2E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 1.17E-04 | 1/°C | ISO 11359-2 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 175 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 160 | °C | ISO 75/Af |
Relative Temp Index, Elec | 65 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |