LNP™ LUBRICOMP™ Compound UCL36ASP

LNP LUBRICOMP UCL36ASP compound is based on Polyphthalamide (PPA) resin containing 30% carbon fiber and 15% PTFE. Added features of this grade include: Internally Lubricated, Electrically Conductive, Heat Stabilized, Wear Resistant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyphthalamide (PPA)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Carbon fiber filled
Electrically Conductive
Heat Stabilized
High stiffness/Strength
High temperature resistance
Wear resistant

Industry

Material previously used in

Automotive Under the Hood
Commercial Appliance
Electronic Components
Home Appliances
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Auto Aftermarket
Electronic Components
EV Infrastructure
Gear/Bearing/Slider
Heavy Vehicles
Lawn/Garden
Sensor

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+01 - 1.E+03	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, unnotched 80104 +23°C*	40	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	7	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 150	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.15	%
Melt Temperature	315 - 330	°C
Front - Zone 3 Temperature	325 - 340	°C
Middle - Zone 2 Temperature	315 - 325	°C
Rear - Zone 1 Temperature	310 - 320	°C
Mold Temperature	140 - 165	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break, 5 mm/min	256	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.3	%	ISO 527
Tensile Modulus, 1 mm/min	25100	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	340	MPa	ISO 178
Flexural Modulus, 2 mm/min	19900	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Mold Shrinkage, flow	0.05 - 0.15	%	SABIC method
Wear Factor Washer	9	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Instr.
Dynamic COF	0.33	-	ASTM D3702 Modified: Instr.
Static COF	0.62	-	ASTM D3702 Modified: Instr.
Density	1.42	g/cm³	ISO 1183
Water Absorption, (23°C/24hrs)	0.4	%	ISO 62-1

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
CTE, 23°C to 60°C, flow	8.E-06	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	5.1E-05	1/°C	ISO 11359-2
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	270	°C	ISO 75/Af

Curve Data

view multipoint data represented visually on graphs.

You may click on the curve legends to select/unselect the curves.

Please login to view graphs, download multi-point data or literature

CAE Cards