LNP™ LUBRICOMP™ Compound UCL36S

LNP LUBRICOMP UCL36S compound is based on Polyphthalamide (PPA) resin containing 15% PTFE, 30% carbon fiber. Added features of this grade include: Internally Lubricated, Wear Resistant, Heat Stabilized, Electrically Conductive.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyphthalamide (PPA)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Carbon fiber filled
Electrically Conductive
Heat Stabilized
High stiffness/Strength
High temperature resistance
Wear resistant

Industry

Material previously used in

Automotive Under the Hood
Commercial Appliance
Electronic Components
Home Appliances
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Lab Ware and Clinical Diagnostics
Medical Device

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+02 - 1.E+06	Ω	ASTM D257

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Yellow Card Link 2	View	-	-
UL Recognized, 94HB Flame Class Rating	1.5	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	939	J/m	ASTM D4812
Izod Impact, notched, 23°C	96	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	39	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	8	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.15	%
Melt Temperature	315 - 330	°C
Front - Zone 3 Temperature	325 - 340	°C
Middle - Zone 2 Temperature	315 - 325	°C
Rear - Zone 1 Temperature	310 - 320	°C
Mold Temperature	150 - 170	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break	216	MPa	ASTM D638
Tensile Strain, break	1.6	%	ASTM D638
Tensile Modulus, 50 mm/min	20130	MPa	ASTM D638
Flexural Stress	324	MPa	ASTM D790
Flexural Modulus	18820	MPa	ASTM D790
Tensile Stress, break	214	MPa	ISO 527
Tensile Strain, break	1.2	%	ISO 527
Flexural Stress	334	MPa	ISO 178
Flexural Modulus	22700	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.41	g/cm³	ASTM D792
Wear Factor Washer	16	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF	0.36	-	ASTM D3702 Modified: Manual
Static COF	0.27	-	ASTM D3702 Modified: Manual

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	279	°C	ASTM D648

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES