FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 |
LNP LUBRICOMP UFL269SA compound is based on Polyphthalamide (PPA) resin containing 30% glass fiber, 10% PTFE. Added features of this grade include: Wear Resistant, Heat Stabilized, Flame Retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 461 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 85 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.15 | % | |
Melt Temperature | 315 - 330 | °C | |
Front - Zone 3 Temperature | 325 - 340 | °C | |
Middle - Zone 2 Temperature | 315 - 325 | °C | |
Rear - Zone 1 Temperature | 310 - 320 | °C | |
Mold Temperature | 150 - 170 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 162 | MPa | ASTM D638 |
Tensile Strain, break | 1.7 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 13650 | MPa | ASTM D638 |
Flexural Stress | 227 | MPa | ASTM D790 |
Flexural Modulus | 12820 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.71 | g/cm³ | ASTM D792 |
Mold Shrinkage, flow, 24 hrs | 0.2 - 0.4 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.7 - 0.9 | % | ASTM D955 |
Wear Factor Washer | 85 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Dynamic COF | 0.47 | - | ASTM D3702 Modified: Manual |
Static COF | 0.38 | - | ASTM D3702 Modified: Manual |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 273 | °C | ASTM D648 |