LNP™ LUBRICOMP™ Compound UFL36AS

LNP LUBRICOMP UFL36AS compound is based on Polyphthalamide (PPA) resin containing 30% glass fiber, 15% PTFE. Added features of this grade include: Heat Stabilized, Internally Lubricated, Wear Resistant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyphthalamide (PPA)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Heat Stabilized
High stiffness/Strength
High temperature resistance
Wear resistant

Industry

Material previously used in

Automotive Under the Hood
Commercial Appliance
Electronic Components
Home Appliances
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Air Intake System
Amusement Machine
Auto Aftermarket
Building Element
Circuit Protection
Electrical
Electronic Components
Engine Component
EV Infrastructure
Exhaust System
Forward Lighting
Gear/Bearing/Slider
Heavy Vehicles
Laundry Dryer
Lawn/Garden
Medical Device
Sensor

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	90	J/m	ASTM D256
Izod Impact, unnotched, 23°C	730	J/m	ASTM D4812
Instrumented Dart Impact Total Energy, 23°C	8	J	ASTM D3763
*Izod Impact, notched 80103 -40°C*	9	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 +23°C*	10	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	50	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -40°C*	45	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	12	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	55	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 150	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.15	%
Melt Temperature	315 - 330	°C
Rear - Zone 1 Temperature	310 - 320	°C
Middle - Zone 2 Temperature	315 - 325	°C
Front - Zone 3 Temperature	325 - 340	°C
Mold Temperature	150 - 170	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 5 mm/min	11200	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	1.7	%	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	189	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	9900	MPa	ASTM D790
Flexural Strength, 1.3 mm/min, 50 mm span	250	MPa	ASTM D790
Tensile Modulus, 1 mm/min	11500	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.3	%	ISO 527
Tensile Stress, break, 5 mm/min	188	MPa	ISO 527
Flexural Modulus, 2 mm/min	10100	MPa	ISO 178
Flexural Modulus, 2 mm/min, 80°C	8400	MPa	ISO 178
Flexural Modulus, 2 mm/min, 100°C	7600	MPa	ISO 178
Flexural Modulus, 2 mm/min, 120°C	5400	MPa	ISO 178
Flexural Modulus, 2 mm/min, 150°C	3800	MPa	ISO 178
Flexural Modulus, 2 mm/min, 180°C	3500	MPa	ISO 178
Flexural Modulus, 2 mm/min, 200°C	3100	MPa	ISO 178
Flexural Strain, break, 2 mm/min	2.8	%	ISO 178
Flexural Strain, break, 2 mm/min, 80°C	3.1	%	ISO 178
Flexural Strain, break, 2 mm/min, 100°C	3.9	%	ISO 178
Flexural Strain, break, 2 mm/min, 120°C	5.3	%	ISO 178
Flexural Strain, break, 2 mm/min, 150°C	5	%	ISO 178
Flexural Strain, break, 2 mm/min, 180°C	4.8	%	ISO 178
Flexural Strain, break, 2 mm/min, 200°C	4.8	%	ISO 178
Flexural Stress, yield, 2 mm/min	260	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 80°C	214	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 100°C	194	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 120°C	141	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 150°C	97	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 180°C	82	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 200°C	71	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.58	-	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.1 - 0.2	%	ASTM D570
Water Absorption, (23°C/24hrs)	0.3 - 0.4	%	ASTM D570
Melt Flow Rate, 340°C/1.2 kgf	28	g/10 min	ASTM D1238
Dynamic COF	0.51	-	ASTM D3702 Modified: Manual
Static COF	0.57	-	ASTM D3702 Modified: Manual
Wear Factor Washer	5	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Density	1.58	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.1 - 0.2	%	ISO 62
Water Absorption, (23°C/24hrs)	0.3 - 0.4	%	ISO 62-1
Melt Volume Rate, MVR at 340°C/1.2 kg	24	cm³/10 min	ISO 1133
Mold Shrinkage, flow	0.2 - 0.4	%	SABIC method
Mold Shrinkage, xflow	0.8 - 1	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	283	°C	ASTM D648
Vicat Softening Temp, Rate B/50	262	°C	ASTM D1525
CTE, -30°C to 30°C, flow	2.1E-05	1/°C	ASTM D696
CTE, -30°C to 30°C, xflow	4.5E-05	1/°C	ASTM D696
Thermal Conductivity	0.24	W/m-K	ASTM D5930
Specific Heat	1722	J/kg-K	ASTM E1269
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	275	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	293	°C	ISO 75/Bf
Vicat Softening Temp, Rate B/50	262	°C	ISO 306
Vicat Softening Temp, Rate B/120	258	°C	ISO 306
CTE, 23°C to 60°C, flow	2.2E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	5.8E-05	1/°C	ISO 11359-2

THIS SITE USES COOKIES

LNP™ LUBRICOMP™ Compound UFL36AS

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Curve Data

CAE Cards

Register for High value Multi-Point Data

THIS SITE USES COOKIES

LNP™ LUBRICOMP™ Compound UFL36AS

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data