LNP LUBRICOMP UFL36SXC compound is based on Polyphthalamide (PPA) resin containing 30% glass fiber, 15% PTFE. Added features of this grade include: Internally Lubricated, Wear Resistant, Heat Stabilized.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 950 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 110 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 6 | J | ASTM D3763 |
| Multiaxial Impact | 2 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 55 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 12 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 | % | |
| Melt Temperature | 315 - 330 | °C | |
| Front - Zone 3 Temperature | 325 - 340 | °C | |
| Middle - Zone 2 Temperature | 315 - 325 | °C | |
| Rear - Zone 1 Temperature | 310 - 320 | °C | |
| Mold Temperature | 150 - 170 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 196 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.5 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 11000 | MPa | ASTM D638 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 275 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 9870 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 191 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 10200 | MPa | ISO 527 |
| Flexural Strength, 2 mm/min | 260 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 9500 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.3 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.8 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.8 | % | ISO 294 |
| Wear Factor Washer | 10 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.56 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.46 | - | ASTM D3702 Modified: Manual |
| Density | 1.55 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 260 | °C | ASTM D648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 260 | °C | ISO 75/Af |