LNP LUBRICOMP UX06425 compound is based on Polyphthalamide (PPA) resin containing 10% glass fiber, 10% PTFE. Added features of this grade include: Wear Resistant, Hot Water Moldable and Heat Stabilized.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 197 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 33 | J/m | ASTM D256 |
| Multiaxial Impact | 1 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy, 23°C | 3 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 12 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 3 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.06 | % | |
| Minimum Moisture Content | 0.03 | % | |
| Melt Temperature | 330 - 345 | °C | |
| Front - Zone 3 Temperature | 325 - 330 | °C | |
| Rear - Zone 1 Temperature | 320 - 325 | °C | |
| Mold Temperature | 65 - 95 | °C | |
| Back Pressure | 0.4 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 89 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.5 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 6610 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 132 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5710 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 85 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 1.4 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 6420 | MPa | ISO 527 |
| Flexural Stress | 126 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 5440 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.34 | - | ASTM D792 |
| Density | 1.33 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.31 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.7 - 0.9 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 1 - 3 | % | ASTM D955 |
| Wear Factor Washer | 15 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Wear Factor Ring | 0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.36 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.37 | - | ASTM D3702 Modified: Manual |
| Moisture Absorption (23°C / 50% RH) | 0.5 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 293 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 260 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 4.1E-05 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 7.5E-05 | 1/°C | ASTM D696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 289 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 254 | °C | ISO 75/Af |