LNP LUBRICOMP UX06427 compound is based on Polyphthalamide (PPA) resin containing 30% carbon fiber, 15% PTFE. Added features of this grade include: Heat Stabilized, Hot Water Moldable, Wear Resistant, Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 646 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 53 | J/m | ASTM D256 |
| Multiaxial Impact | 2 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.06 | % | |
| Minimum Moisture Content | 0.03 | % | |
| Melt Temperature | 330 - 345 | °C | |
| Front - Zone 3 Temperature | 325 - 330 | °C | |
| Rear - Zone 1 Temperature | 320 - 325 | °C | |
| Mold Temperature | 65 - 95 | °C | |
| Back Pressure | 0.4 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 224 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.2 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 25200 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 311 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 17200 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 227 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 22770 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/min | 19640 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.4 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.06 - 0.09 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.6 - 0.9 | % | ASTM D955 |
| Wear Factor Washer | 26 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.34 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.33 | - | ASTM D3702 Modified: Manual |
| Density | 1.41 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.6 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 296 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 284 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 2.2E-05 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 3.4E-05 | 1/°C | ASTM D696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 298 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 284 | °C | ISO 75/Af |