LNP LUBRICOMP WL002 compound is based on Polybutylene Terephthalate (PBT) resin containing 10% PTFE. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 880 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 39 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 6 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 53 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 3 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 240 - 265 | °C | |
| Front - Zone 3 Temperature | 260 - 270 | °C | |
| Middle - Zone 2 Temperature | 245 - 255 | °C | |
| Rear - Zone 1 Temperature | 220 - 230 | °C | |
| Mold Temperature | 80 - 100 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 52 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 51 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 9.3 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 12 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2780 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2640 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 51 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 51 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 9.8 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 10.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2900 | MPa | ISO 527 |
| Flexural Stress | 78 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2340 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 2 - 4 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 2 - 4 | % | ASTM D955 |
| Wear Factor Washer | 25 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Wear Factor Ring | 2 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.35 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.31 | - | ASTM D3702 Modified: Manual |
| Density | 1.38 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.09 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 182 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 58 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 9.8E-05 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 9.9E-05 | 1/°C | ASTM D696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 160 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 57 | °C | ISO 75/Af |