LNP LUBRICOMP XFL21R compound is based on Amorphous Nylon resin containing 5% glass fiber, 10% PTFE. Added features of this grade include: Wear Resistant, Mold Release.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 506 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 6 - 12 | Hrs | |
| Maximum Moisture Content | 0.1 | % | |
| Melt Temperature | 260 - 300 | °C | |
| Front - Zone 3 Temperature | 290 - 300 | °C | |
| Middle - Zone 2 Temperature | 270 - 290 | °C | |
| Rear - Zone 1 Temperature | 260 - 270 | °C | |
| Mold Temperature | 50 - 100 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 84 | MPa | ASTM D638 |
| Tensile Strain, break | 4.1 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 3730 | MPa | ASTM D638 |
| Flexural Stress | 131 | MPa | ASTM D790 |
| Flexural Modulus | 3900 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.7 | % | ASTM D955 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 138 | °C | ASTM D648 |