LNP LUBRICOMP YL003 compound is based on Polyester Elastomer resin containing 15% PTFE. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 455 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 312 | J/m | ASTM D256 |
| Multiaxial Impact | 24 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy, 23°C | 25 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 42 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.1 | % | |
| Melt Temperature | 215 - 240 | °C | |
| Front - Zone 3 Temperature | 225 - 240 | °C | |
| Middle - Zone 2 Temperature | 205 - 215 | °C | |
| Rear - Zone 1 Temperature | 180 - 195 | °C | |
| Mold Temperature | 25 - 55 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 43 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 14.2 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 230 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 230 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 14 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 43.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 240 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/min | 220 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.28 | - | ASTM D792 |
| Density | 1.27 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.33 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 1 - 3 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 1 - 3 | % | ASTM D955 |
| Moisture Absorption (23°C / 50% RH) | 0.47 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, -30°C to 30°C, flow | 1.72E-04 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 1.88E-04 | 1/°C | ASTM D696 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 21 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.1 | % | |
| Melt Temperature | 215 - 240 | °C | |
| Front - Zone 3 Temperature | 225 - 240 | °C | |
| Middle - Zone 2 Temperature | 205 - 215 | °C | |
| Rear - Zone 1 Temperature | 180 - 195 | °C | |
| Mold Temperature | 25 - 55 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 50 mm/min | 24 | MPa | ISO 527 |
| Tensile Strain, break, 50 mm/min | 455 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 180 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 12 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 230 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage, flow | 2.3 | % | SABIC method |
| Mold Shrinkage, flow, 24 hrs | 1.5 - 2.5 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.5 - 2.5 | % | ISO 294 |
| Density | 1.28 | g/cm³ | ISO 1183 |