FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 3 | mm | UL 94 |
UL Recognized, 94V-2 Flame Class Rating | ≥1.5 | mm | UL 94 |
LNP LUBRILOY D20009 compound is based on Polycarbonate (PC) resin containing proprietary lubricant. Added features of this grade include: Flame Retardant, Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 3 | mm | UL 94 |
UL Recognized, 94V-2 Flame Class Rating | ≥1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | NB | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 699 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 100 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 305 - 315 | °C | |
Front - Zone 3 Temperature | 305 - 315 | °C | |
Middle - Zone 2 Temperature | 300 - 310 | °C | |
Rear - Zone 1 Temperature | 295 - 305 | °C | |
Mold Temperature | 65 - 95 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 61 | MPa | ASTM D638 |
Tensile Strain, break | 84 | % | ASTM D638 |
Flexural Stress | 87 | MPa | ASTM D790 |
Flexural Modulus | 2280 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.23 | g/cm³ | ASTM D792 |
Mold Shrinkage, flow, 24 hrs | 0.6 - 0.8 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.6 - 0.8 | % | ASTM D955 |
Wear Factor Washer | 56 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Dynamic COF | 0.25 | - | ASTM D3702 Modified: Manual |
Static COF | 0.13 | - | ASTM D3702 Modified: Manual |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 121 | °C | ASTM D648 |
Relative Temp Index, Elec | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 3 | mm | UL 94 |
UL Recognized, 94V-2 Flame Class Rating | ≥1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | NB | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 699 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 305 - 325 | °C | |
Front - Zone 3 Temperature | 320 - 330 | °C | |
Middle - Zone 2 Temperature | 310 - 320 | °C | |
Rear - Zone 1 Temperature | 295 - 305 | °C | |
Mold Temperature | 80 - 110 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 61 | MPa | ASTM D638 |
Tensile Strain, break | 84 | % | ASTM D638 |
Flexural Stress | 87 | MPa | ASTM D790 |
Flexural Modulus | 2280 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.23 | g/cm³ | ASTM D792 |
Mold Shrinkage, flow, 24 hrs | 0.6 - 0.8 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.6 - 0.8 | % | ASTM D955 |
Wear Factor Washer | 56 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Dynamic COF | 0.25 | - | ASTM D3702 Modified: Manual |
Static COF | 0.13 | - | ASTM D3702 Modified: Manual |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 121 | °C | ASTM D648 |
Relative Temp Index, Elec | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |