LNP LUBRILOY K2000XXL compound is based on Acetal (POM) copolymer resin containing proprietary, non-PTFE lubrication. Added features include Wear Resistant and Low Extractable.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 41 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 200 - 215 | °C | |
| Front - Zone 3 Temperature | 210 - 220 | °C | |
| Middle - Zone 2 Temperature | 195 - 205 | °C | |
| Rear - Zone 1 Temperature | 175 - 190 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw speed (Circumferential speed) | 30 - 60 | m/s |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Modulus, 50 mm/min | 2384 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 45 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 13 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 17 | % | ASTM D638 |
| Tensile Nominal Strain, brk, Type I, 50 mm/min | 10 | % | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2040 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Moisture Absorption (23°C / 50% RH) | 0.093 | % | ISO 62 |
| Mold Shrinkage, flow | 2.99 | % | SABIC method |
| Mold Shrinkage, xflow | 2.55 | % | SABIC method |
| Dynamic COF | 0.32 | - | ASTM D3702 Modified: Manual |
| Wear Factor (K) | 5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Melt Flow Rate, 190°C/2.16 kgf | 19 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 84 | °C | ASTM D648 |