LNP™ LUBRILOY™ Compound K8000XXL

LNP LUBRILOY K8000XXL compound is based on Acetal (POM) copolymer resin contain proprietary non-PTFE lubrication. Added features include Wear Resistant, Low Extractable.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Acetal (POM) Copolymer

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Low Extractable
No PFAS intentionally added
Wear resistant

Industry

Material previously used in

Food & Beverage
General Healthcare
Home Appliances
Industrial General
Water Management

Applications

Possible usage of material

Conveyor

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	41	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Melt Temperature	200 - 215	°C
Front - Zone 3 Temperature	210 - 220	°C
Middle - Zone 2 Temperature	195 - 205	°C
Rear - Zone 1 Temperature	175 - 190	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw speed (Circumferential speed)	30 - 60	m/s

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 50 mm/min	2384	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	45	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	13	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	17	%	ASTM D638
Tensile Nominal Strain, brk, Type I, 50 mm/min	10	%	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	2040	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Moisture Absorption (23°C / 50% RH)	0.093	%	ISO 62
Mold Shrinkage, flow	2.99	%	SABIC method
Mold Shrinkage, xflow	2.55	%	SABIC method
Dynamic COF	0.32	-	ASTM D3702 Modified: Manual
Wear Factor (K)	5	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Melt Flow Rate, 190°C/2.16 kgf	19	g/10 min	ASTM D1238

Physical Properties

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.39	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	84	°C	ASTM D648

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience