LNP™ LUBRILOY™ RC206 compound is based on Nylon 6/6 resin containing 30% carbon fiber and proprietary lubricant. Added features include; internally lubricated, wear resistant, PTFE not intentionally added.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 880 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 112 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | 55 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 280 - 305 | °C | |
| Rear - Zone 1 Temperature | 265 - 275 | °C | |
| Middle - Zone 2 Temperature | 280 - 295 | °C | |
| Front - Zone 3 Temperature | 295 - 305 | °C | |
| Mold Temperature | 95 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 236 | MPa | ASTM D638 |
| Tensile Strain, break | 2.6 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 22600 | MPa | ASTM D638 |
| Flexural Stress | 340 | MPa | ASTM D790 |
| Flexural modulus | 18800 | MPa | ASTM D790 |
| Tensile Stress, break | 236 | MPa | ISO 527 |
| Tensile Strain, break | 2.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 22400 | MPa | ISO 527 |
| Flexural Stress | 331 | MPa | ISO 178 |
| Flexural Modulus | 18200 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.4 - 0.6 | % | ISO 62 |
| Melt Volume Rate, MVR at 275°C/5 kg | 16 | cm³/10 min | ISO 1133 |
| Wear Factor Washer | 20 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Instr. |
| Dynamic COF | 0.26 | - | ASTM D3702 Modified: Instr. |
| Static COF | 0.51 | - | ASTM D3702 Modified: Instr. |
| Mold Shrinkage, flow | 0.1 - 0.3 | % | SABIC method |
| Mold Shrinkage, xflow | 0.6 - 0.8 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 254 | °C | ISO 75/Af |
| CTE, 23°C to 60°C, flow | 6.5E-06 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 8.5E-05 | 1/°C | ISO 11359-2 |