LNP™ LUBRILOY™ Compound UF206

LNP™ LUBRILOY™ UF206 compound is based on Polyphthalamide (PPA) resin containing 30% glass fiber and proprietary lubricant. Added features include; internally lubricated, wear resistant, PTFE not intentionally added.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyphthalamide (PPA)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Lubricated
Wear and Friction

Industry

Material previously used in

Automotive Under the Hood
Commercial Appliance
Electronic Components
Home Appliances
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Commercial Appliance

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94HB Flame Class Rating	0.8	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	353	J/m	ASTM D4812
Izod Impact, notched, 23°C	46	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	31	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	5	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 150	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.15	%
Melt Temperature	315 - 330	°C
Rear - Zone 1 Temperature	310 - 320	°C
Middle - Zone 2 Temperature	315 - 325	°C
Front - Zone 3 Temperature	325 - 340	°C
Mold Temperature	150 - 170	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break	102	MPa	ASTM D638
Tensile Strain, break	1.9	%	ASTM D638
Tensile Modulus, 5 mm/min	9500	MPa	ASTM D638
Flexural Stress	138	MPa	ASTM D790
Flexural modulus	7100	MPa	ASTM D790
Tensile Stress, break	106	MPa	ISO 527
Tensile Strain, break	2.0	%	ISO 527
Tensile Modulus, 1 mm/min	9600	MPa	ISO 527
Flexural Stress	155	MPa	ISO 178
Flexural Modulus	8400	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.36	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)	2.0 - 3.5	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.5 - 0.8	%	ISO 62
Melt Volume Rate, MVR at 340°C/2.16 kg	17	cm³/10 min	ISO 1133
Wear Factor Washer	35	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Instr.
Dynamic COF	0.38	-	ASTM D3702 Modified: Instr.
Static COF	0.56	-	ASTM D3702 Modified: Instr.
Mold Shrinkage, flow	0.2 - 0.4	%	SABIC method
Mold Shrinkage, xflow	0.6 - 1.0	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	245	°C	ISO 75/Af
CTE, 23°C to 60°C, flow	1.9E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	6.7E-05	1/°C	ISO 11359-2
Relative Temp Index, Elec	85	°C	UL 746B
Relative Temp Index, Mech w/impact	85	°C	UL 746B
Relative Temp Index, Mech w/o impact	85	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas