LNP™ LUBRILOY™ Compound UX99725

LNP LUBRILOY UX99725 compound is based on Polyphthalamide (PPA) resin containing proprietary lubricant. Added features of this grade include: Wear Resistant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyphthalamide (PPA)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High temperature resistance
No PFAS intentionally added
Wear resistant

Industry

Material previously used in

Automotive Exteriors
Automotive Under the Hood

Applications

Possible usage of material

Brake System
Enclosure/Housing/Cover
Recreational Vehicle
belt tensioner
damping band

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	118	J/m	ASTM D256
*Izod Impact, notched 80104 +23°C*	13	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	15	kJ/m²	ISO 179/1eA

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	4	Hrs
Melt Temperature	315 - 330	°C
Front - Zone 3 Temperature	325 - 340	°C
Middle - Zone 2 Temperature	315 - 325	°C
Rear - Zone 1 Temperature	310 - 320	°C
Mold Temperature	150 - 170	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	68	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	60	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	8	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	20	%	ASTM D638
Tensile Modulus, 5 mm/min	2244	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	2010	MPa	ASTM D790
Flexural Stress at 5% strain, 1.3 mm/min, 50 mm span	82	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	66	MPa	ISO 527
Tensile Stress, break, 5 mm/min	64	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	7	%	ISO 527
Tensile Strain, break, 5 mm/min	9	%	ISO 527
Tensile Modulus, 1 mm/min	2153	MPa	ISO 527
Flexural Modulus, 2 mm/min	2180	MPa	ISO 178
Flexural Strength, 2 mm/min	94	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.119	-	ASTM D792
Density	1.11	g/cm³	ISO 1183
Water Absorption, (23°C/24hrs)	0.5	%	ISO 62-1
Melt Volume Rate, MVR at 330°C/2.16kg	6	cm³/10 min	ISO 1133
Mold Shrinkage, flow	1.2 - 1.7	%	SABIC method
Mold Shrinkage, xflow	1.5 - 2	%	SABIC method
Wear Factor Washer	35	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF	0.15	-	ASTM D3702 Modified: Manual
Static COF	0.14	-	ASTM D3702 Modified: Manual

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	140	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	121	°C	ASTM D648
CTE, -40°C to 40°C, flow	9.7E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	9.2E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	9.7E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	9.2E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	151	°C	ISO 306
Vicat Softening Temp, Rate B/120	151	°C	ISO 306
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	139	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	119	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES