LNP™ LUBRILOY™ Compound W8000

LNP LUBRILOY W8000 compound is a PBT based, internally lubricated injection molding grade. This compound offers improved wear and friction performance without the use of intentionally added PFAS materials.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polybutylene Terephthalate (PBT)

Processing Technology

Injection Molding
Extrusion
Compression molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Wear resistant

Industry

Material previously used in

Automotive Under the Hood
Commercial Appliance
Consumer Goods
Electronic Components
Furniture
Home Appliances
Industrial General
Printer Copier
Sport/Leisure

Applications

Possible usage of material

Automotive
Under the hood
Amusement Machine
ATM/Ticket Machine
Commercial Appliance
Conveyor
Document Handling
Doors Hardware/Trim
Gear/Bearing/Slider
Vending Machine

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	3.7	kJ/m²	ISO 180/1A
Izod Impact, notched, 23°C	26	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.05	%
Melt Temperature	240 - 265	°C
Rear - Zone 1 Temperature	220 - 230	°C
Middle - Zone 2 Temperature	245 - 255	°C
Front - Zone 3 Temperature	260 - 270	°C
Mold Temperature	80 - 100	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 1 mm/min	2487	MPa	ISO 527
Tensile Stress, yield, 50 mm/min	52	MPa	ISO 527
Tensile Stress, break, 50 mm/min	48	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	6	%	ISO 527
Tensile Strain, break, 50 mm/min	14	%	ISO 527
Flexural Modulus, 2 mm/min	2300	MPa	ISO 178
Flexural Stress, yield, 2 mm/min	78	MPa	ISO 178
Flexural Stress, break, 2 mm/min	77	MPa	ISO 178
Tensile Modulus, 50 mm/min	2469	MPa	ASTM D638
Tensile Stress, yld, Type I, 50 mm/min	52	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	47	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	6	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	18	%	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	2390	MPa	ASTM D790
Flexural Stress, yld, 1.3 mm/min, 50 mm span	78	MPa	ASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	80	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Moisture Absorption (23°C / 50% RH)	0.028	%	ISO 62
Moisture Absorption, (50% RH, Equilibrium)	0.028	%	ASTM D570
Mold Shrinkage, flow	2.1	%	SABIC method
Mold Shrinkage, xflow	2.2	%	SABIC method
Specific Gravity	1.29	-	ASTM D792
Melt Flow Rate, 250°C/5.0 kg	48	g/10 min	ISO 1133
Wear Factor Washer	40	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF	0.48	-	ASTM D3702 Modified: Manual

PROFILE EXTRUSION

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.05	%
Melt Temperature	250 - 275	°C
Barrel - Zone 1 Temperature	250 - 260	°C
Barrel - Zone 2 Temperature	250 - 265	°C
Barrel - Zone 3 Temperature	250 - 265	°C
Barrel - Zone 4 Temperature	250 - 265	°C
Die Temperature	266 - 266	°C

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	52	°C	ASTM D648

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES