LNP LUBRILOY ZX06315 is a compound based on PPE+PS Blend resin containing Flame Retardant, Proprietary Lubricant. Added features of this material include: Internally Lubricated, Non-Brominated & Non-Chlorinated Flame Retardant, Flame Retardant, high HDT.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 230 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Melt Temperature | 270 - 295 | °C | |
| Nozzle Temperature | 265 - 275 | °C | |
| Front - Zone 3 Temperature | 265 - 275 | °C | |
| Middle - Zone 2 Temperature | 260 - 270 | °C | |
| Rear - Zone 1 Temperature | 255 - 265 | °C | |
| Mold Temperature | 60 - 95 | °C | |
| Back Pressure | 0.2 - 0.4 | MPa | |
| Screw Speed | 40 - 100 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 63 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 50 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 11.9 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2270 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 93 | MPa | ASTM D790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 91 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2190 | MPa | ASTM D790 |
| Hardness, Rockwell R | 115 | - | ASTM D785 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.94 - 0.96 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.91 - 0.93 | % | ASTM D955 |
| Wear Factor Washer | 65 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.21 | - | ASTM D3702 Modified: Manual |
| Melt Volume Rate, MVR at 280°C/10.0 kg | 38 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 124 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 129 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 7.2E-04 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 8.6E-04 | 1/°C | ASTM E831 |
| Relative Temp Index, Elec | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |