LNP STAT-KON CD000I compound is based on Polystyrene (PS) resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive, High Impact.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 744 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 82 | J/m | ASTM D256 |
| Multiaxial Impact | 15 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy, 23°C | 18 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 31 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 250 | °C | |
| Front - Zone 3 Temperature | 265 - 275 | °C | |
| Middle - Zone 2 Temperature | 245 - 255 | °C | |
| Rear - Zone 1 Temperature | 220 - 230 | °C | |
| Mold Temperature | 40 - 65 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 23 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 16 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 1.2 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 9.7 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 2280 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 42 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2280 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 23 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 17 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 1.2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 7.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2120 | MPa | ISO 527 |
| Flexural Stress | 40 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2100 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.08 | - | ASTM D792 |
| Density | 1.08 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.1 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.3 - 0.7 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 - 0.7 | % | ASTM D955 |
| Moisture Absorption (23°C / 50% RH) | 0.13 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 87 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 75 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 9.8E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 1.07E-04 | 1/°C | ASTM E831 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 87 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 78 | °C | ISO 75/Af |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 384 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 48 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 20 | MPa | ASTM D638 |
| Tensile Strain, break | 6.6 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2170 | MPa | ASTM D638 |
| Flexural Stress | 41 | MPa | ASTM D790 |
| Flexural Modulus | 2690 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 75 | °C | ASTM D648 |