LNP™ STAT-KON™ Compound DC10EPFR

LNP STAT-KON DC10EPFR compound is based on Polycarbonate (PC) resin containing 10% carbon fiber. Added features of this grade include: Flame Retardant, Electrically Conductive, Exceptional Processing.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Electrically Conductive
Flame Retardant
High Flow

Industry

Material previously used in

Electrical
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

ATM/Ticket Machine
Circuit Protection
Data Management

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+02 - 1.E+06	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	546	J/m	ASTM D4812
Izod Impact, notched, 23°C	59	J/m	ASTM D256
Multiaxial Impact	4	J	ISO 6603
Instrumented Dart Impact Total Energy, 23°C	23	J	ASTM D3763
*Izod Impact, unnotched 80104 +23°C*	33	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	6	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	305 - 325	°C
Front - Zone 3 Temperature	320 - 330	°C
Middle - Zone 2 Temperature	310 - 320	°C
Rear - Zone 1 Temperature	295 - 305	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	120	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.5	%	ASTM D638
Tensile Modulus, 5 mm/min	7940	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	176	MPa	ASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	173	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	6800	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	118	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.6	%	ISO 527
Tensile Modulus, 1 mm/min	7570	MPa	ISO 527
Flexural Strength, 2 mm/min	169	MPa	ISO 178
Flexural Modulus, 2 mm/min	6800	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.25	-	ASTM D792
Density	1.24	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.11	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.1 - 0.3	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.4 - 0.6	%	ASTM D955
Moisture Absorption (23°C / 50% RH)	0.17	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	141	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	138	°C	ASTM D648
CTE, -30°C to 30°C, flow	4.2E-05	1/°C	ASTM D696
CTE, -30°C to 30°C, xflow	4.6E-05	1/°C	ASTM D696
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	141	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	137	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES