LNP STAT-KON DD0001 compound is based on Polycarbonate (PC) resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive, Non-Brominated, Non-Chlorinated Flame Retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 550 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 23 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 1 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 36 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 2 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 255 - 290 | °C | |
| Front - Zone 3 Temperature | 260 - 270 | °C | |
| Middle - Zone 2 Temperature | 255 - 265 | °C | |
| Rear - Zone 1 Temperature | 250 - 260 | °C | |
| Mold Temperature | 40 - 65 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 64 | MPa | ASTM D638 |
| Tensile Strain, break | 3.6 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 3450 | MPa | ASTM D638 |
| Flexural Stress | 116 | MPa | ASTM D790 |
| Flexural Modulus | 3510 | MPa | ASTM D790 |
| Tensile Stress, break | 64 | MPa | ISO 527 |
| Tensile Strain, break | 3.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3750 | MPa | ISO 527 |
| Flexural Stress | 103 | MPa | ISO 178 |
| Flexural Modulus | 3520 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.1 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.4 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.39 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 | % | ISO 294 |
| Moisture Absorption (23°C / 50% RH) | 0.14 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 86 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 82 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 5.22E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 5.23E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 5.22E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 5.24E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 88 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 82 | °C | ISO 75/Af |