ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+04 - 1.E+10 | Ω | ASTM D257 |
LNP STAT-KON DD0009 compound is based on Polycarbonate (PC) resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive, Flame Retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+04 - 1.E+10 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 1556 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 68 | J/m | ASTM D256 |
Instrumented Dart Impact Energy @ peak, 23°C | 10 | J | ASTM D3763 |
Multiaxial Impact | 5 | J | ISO 6603 |
Izod Impact, unnotched 80*10*4 +23°C | 70 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 48 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 270 - 295 | °C | |
Nozzle Temperature | 265 - 290 | °C | |
Front - Zone 3 Temperature | 270 - 295 | °C | |
Middle - Zone 2 Temperature | 260 - 280 | °C | |
Rear - Zone 1 Temperature | 250 - 270 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Mold Temperature | 70 - 95 | °C | |
Screw Speed | 40 - 70 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield | 61 | MPa | ASTM D638 |
Tensile Stress, break | 53 | MPa | ASTM D638 |
Tensile Strain, yield | 1.2 | % | ASTM D638 |
Tensile Strain, break | 5.6 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2820 | MPa | ASTM D638 |
Flexural Stress | 108 | MPa | ASTM D790 |
Flexural Modulus | 2820 | MPa | ASTM D790 |
Tensile Stress, yield | 62 | MPa | ISO 527 |
Tensile Stress, break | 57 | MPa | ISO 527 |
Tensile Strain, yield | 4.1 | % | ISO 527 |
Tensile Strain, break | 7.5 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2810 | MPa | ISO 527 |
Flexural Stress | 102 | MPa | ISO 178 |
Flexural Modulus | 2880 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.32 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.18 | % | ASTM D570 |
Mold Shrinkage, flow, 24 hrs | 0.8 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.7 | % | ASTM D955 |
Mold Shrinkage, flow, 24 hrs | 0.75 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 0.72 | % | ISO 294 |
Moisture Absorption (23°C / 50% RH) | 0.27 | % | ISO 62 |
Melt Volume Rate, MVR at 300°C/5.0 kg | 31 | cm³/10 min | ASTM D1238 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 141 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 132 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 5.36E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 5.67E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 5.36E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 5.67E-05 | 1/°C | ISO 11359-2 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 139 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 131 | °C | ISO 75/Af |
Relative Temp Index, Elec | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |