LNP STAT-KON DD0009E compound is based on Polycarbonate (PC) resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive, Flame Retardant, Easy Molding.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+01 - 1.E+05 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | 1.6 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 2000 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D256 |
| Multiaxial Impact | 5 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy, 23°C | 12 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 99 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 305 - 325 | °C | |
| Front - Zone 3 Temperature | 320 - 330 | °C | |
| Middle - Zone 2 Temperature | 310 - 320 | °C | |
| Rear - Zone 1 Temperature | 295 - 305 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 61 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 61 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3.8 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 4.1 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 3050 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 107 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3050 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 63 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 4.3 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 8.6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3050 | MPa | ISO 527 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2890 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.32 | - | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.16 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.4 - 0.6 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.6 - 0.8 | % | ASTM D955 |
| Density | 1.32 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.24 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 141 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 130 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 7.E-06 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 7.E-06 | 1/°C | ASTM D696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 141 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 128 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+01 - 1.E+05 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | 1.6 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 2000 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 62 | MPa | ASTM D638 |
| Tensile Strain, break | 4 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 3050 | MPa | ASTM D638 |
| Flexural Stress | 96 | MPa | ASTM D790 |
| Flexural Modulus | 3170 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 130 | °C | ASTM D648 |
| Relative Temp Index, Elec | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.