ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
LNP STAT-KON DD0009PC compound is based on Polycarbonate (PC) resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive, Exceptional Processing, Flame Retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 2100 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 119 | J/m | ASTM D256 |
Instrumented Dart Impact Energy @ peak, 23°C | 15 | J | ASTM D3763 |
Multiaxial Impact | 35 | J | ISO 6603 |
Izod Impact, unnotched 80*10*4 +23°C | 137 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 8 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 270 - 295 | °C | |
Rear - Zone 1 Temperature | 250 - 270 | °C | |
Middle - Zone 2 Temperature | 260 - 280 | °C | |
Front - Zone 3 Temperature | 270 - 295 | °C | |
Nozzle Temperature | 265 - 290 | °C | |
Mold Temperature | 70 - 95 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm | |
Vent Depth | 0.025 - 0.076 | mm | |
Shot to Cylinder Size | 40 - 60 | % |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield | 61 | MPa | ASTM D638 |
Tensile Stress, break | 53 | MPa | ASTM D638 |
Tensile Strain, yield | 4.9 | % | ASTM D638 |
Tensile Strain, break | 11 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2620 | MPa | ASTM D638 |
Flexural Stress | 101 | MPa | ASTM D790 |
Flexural Modulus | 2820 | MPa | ASTM D790 |
Tensile Stress, yield | 59 | MPa | ISO 527 |
Tensile Stress, break | 51 | MPa | ISO 527 |
Tensile Strain, yield | 4.6 | % | ISO 527 |
Tensile Strain, break | 11 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2700 | MPa | ISO 527 |
Flexural Stress | 98 | MPa | ISO 178 |
Flexural Modulus | 2900 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.29 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.14 | % | ASTM D570 |
Mold Shrinkage, flow, 24 hrs | 0.8 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.8 | % | ASTM D955 |
Mold Shrinkage, flow, 24 hrs | 0.77 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 0.79 | % | ISO 294 |
Moisture Absorption (23°C / 50% RH) | 0.23 | % | ISO 62 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 140 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 128 | °C | ASTM D648 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 130 | °C | ISO 75/Af |
Relative Temp Index, Elec | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |