LNP™ STAT-KON™ Compound DE0021E

LNP STAT-KON DE0021E compound is based on Polycarbonate (PC) resin containing 10% carbon fiber. Added features of this grade include: Easy Molding, Non-Brominated, Non-Chlorinated Flame Retardant, Electrically Conductive.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Carbon fiber filled
Electrically Conductive
Flame Retardant
Good Processability
High stiffness/Strength
Non Cl/Br flame retardant

Industry

Material previously used in

Electronic Components
Material Handling

Applications

Possible usage of material

Data Management
Document Handling
Enclosures
Personal Computing
Pump
Semiconductor
Vacuum Cleaner
Wearables
Wiring Devices
atm
cooling fan
air premixing
gas blower impeller
flow meter enclosure
seed disc
office equipment
paper handling
household appliance
domestic appliance

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+02 - 1.E+06	Ω	ASTM D257

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Yellow Card Link 2	View	-	-
UL Recognized, 94V-0 Flame Class Rating	≥1.5	mm	UL 94
UL Recognized, 94V-1 Flame Class Rating	≥1.2	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	347	J/m	ASTM D4812
Izod Impact, notched, 23°C	37	J/m	ASTM D256
Instrumented Dart Impact Energy @ peak, 23°C	9	J	ASTM D3763
Multiaxial Impact	7	J	ISO 6603
*Izod Impact, unnotched 80104 +23°C*	31	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	7	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	255 - 290	°C
Front - Zone 3 Temperature	260 - 270	°C
Middle - Zone 2 Temperature	255 - 265	°C
Rear - Zone 1 Temperature	250 - 260	°C
Mold Temperature	40 - 65	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break	114	MPa	ASTM D638
Tensile Strain, break	1.8	%	ASTM D638
Tensile Modulus, 50 mm/min	9160	MPa	ASTM D638
Flexural Stress	170	MPa	ASTM D790
Flexural Modulus	8210	MPa	ASTM D790
Tensile Stress, break	112	MPa	ISO 527
Tensile Strain, break	2.1	%	ISO 527
Tensile Modulus, 1 mm/min	9360	MPa	ISO 527
Flexural Stress	169	MPa	ISO 178
Flexural Modulus	8500	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.27	g/cm³	ASTM D792
Mold Shrinkage, flow, 24 hrs	0.1 - 0.3	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.2 - 0.4	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	0.06 - 0.32	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.29 - 0.43	%	ISO 294
Density	1.27	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.1	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	93	°C	ASTM D648
CTE, -40°C to 40°C, flow	1.67E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	6.08E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	1.67E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	6.09E-05	1/°C	ISO 11359-2
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	96	°C	ISO 75/Af
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

Register for High value Multi-Point Data