ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
LNP STAT-KON DE0026E compound is based on Polycarbonate (PC) resin containing 10% carbon fiber. Added features of this grade include Non-Chlorinated, Non-Brominated Flame Retardant, Electrically Conductive and Easy Molding.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 2 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 305 - 325 | °C | |
Front - Zone 3 Temperature | 320 - 330 | °C | |
Middle - Zone 2 Temperature | 310 - 320 | °C | |
Rear - Zone 1 Temperature | 295 - 305 | °C | |
Mold Temperature | 80 - 110 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield, 5 mm/min | 117 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 2.7 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 8000 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 182 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 7000 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.23 | g/cm³ | ISO 1183 |
Mold Shrinkage, flow | 0.1 - 0.3 | % | SABIC method |
Mold Shrinkage, xflow | 0.2 - 0.4 | % | SABIC method |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
CTE, 23°C to 60°C, flow | 1.8E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 7.4E-05 | 1/°C | ISO 11359-2 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 143 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 140 | °C | ISO 75/Af |
Relative Temp Index, Elec | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.