ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.E+04 - 1.E+07 | Ω.cm | ASTM D257 |
Surface Resistivity | 1.E+03 - 1.E+06 | Ω | ASTM D257 |
LNP STAT-KON DE0029 compound is based on Polycarbonate (PC) resin containing 10% carbon fiber. Added features of this grade include: Electrically Conductive, Flame Retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.E+04 - 1.E+07 | Ω.cm | ASTM D257 |
Surface Resistivity | 1.E+03 - 1.E+06 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 490 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 58 | J/m | ASTM D256 |
Izod Impact, unnotched 80*10*4 +23°C | 32 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 305 - 325 | °C | |
Front - Zone 3 Temperature | 320 - 330 | °C | |
Middle - Zone 2 Temperature | 310 - 320 | °C | |
Rear - Zone 1 Temperature | 295 - 305 | °C | |
Mold Temperature | 80 - 110 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 104 | MPa | ASTM D638 |
Tensile Strain, break | 5.9 | % | ASTM D638 |
Flexural Stress | 158 | MPa | ASTM D790 |
Flexural Modulus | 7580 | MPa | ASTM D790 |
Tensile Stress, break | 104 | MPa | ISO 527 |
Tensile Strain, break | 6.2 | % | ISO 527 |
Flexural Stress | 149 | MPa | ISO 178 |
Flexural Modulus | 7400 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.29 | g/cm³ | ASTM D792 |
Mold Shrinkage, flow, 24 hrs | 0.1 - 0.3 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.3 - 0.5 | % | ASTM D955 |
Mold Shrinkage, flow, 24 hrs | 0.19 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 0.39 | % | ISO 294 |
Density | 1.29 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 145 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 142 | °C | ASTM D648 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 145 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 142 | °C | ISO 75/Af |
Relative Temp Index, Elec | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |