LNP STAT-KON DE003Z compound is based on Polycarbonate (PC) resin containing 15% carbon fiber. Added features of this grade include: Electrically Conductive, Extrusion grade.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 623 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 98 | J/m | ASTM D256 |
| Multiaxial Impact | 4 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy, 23°C | 24 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 39 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 305 - 325 | °C | |
| Front - Zone 3 Temperature | 320 - 330 | °C | |
| Middle - Zone 2 Temperature | 310 - 320 | °C | |
| Rear - Zone 1 Temperature | 295 - 305 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 134 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 134 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.4 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 11320 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 200 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 9120 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 130 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 10660 | MPa | ISO 527 |
| Flexural Stress | 191 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 9290 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.26 | - | ASTM D792 |
| Density | 1.253 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.13 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.1 - 0.3 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 - 0.6 | % | ASTM D955 |
| Moisture Absorption (23°C / 50% RH) | 0.21 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 147 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 144 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 2.2E-05 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 4.8E-05 | 1/°C | ASTM D696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 147 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 143 | °C | ISO 75/Af |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Instrumented Dart Impact Energy @ peak, 23°C | 15 | J | ASTM D3763 |
| Multiaxial Impact | 104 | J | ISO 6603 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 144 | °C | ASTM D648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 143 | °C | ISO 75/Af |