LNP STAT-KON DE0049F compound is based on Polycarbonate (PC) resin containing 20% carbon fiber. Added features of this grade include: Electrically Conductive, Flame Retardant, Superior Molding.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+01 - 1.E+03 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 488 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 47 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | 29 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 305 - 325 | °C | |
| Front - Zone 3 Temperature | 320 - 330 | °C | |
| Middle - Zone 2 Temperature | 310 - 320 | °C | |
| Rear - Zone 1 Temperature | 295 - 305 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 137 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 137 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 1.9 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.9 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 13420 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 190 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 11550 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 134 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 134 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 1.6 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 14970 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 166 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 166 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 11650 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.13 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.1 - 0.5 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.3 - 0.7 | % | ASTM D955 |
| Density | 1.33 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.18 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 146 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 143 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 1.23E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 6.79E-05 | 1/°C | ASTM E831 |
| CTE, 23°C to 60°C, flow | 1.23E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 6.79E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 148 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 144 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature