ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
LNP STAT-KON DEL139P compound is based on Polycarbonate (PC) resin containing 15% carbon fiber, 5% PTFE. Added features of this grade include: Electrically Conductive, Exceptional Processing, Flame Retardant, Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 433 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 45 | J/m | ASTM D256 |
Multiaxial Impact | 2 | J | ISO 6603 |
Izod Impact, unnotched 80*10*4 +23°C | 27 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 305 - 325 | °C | |
Front - Zone 3 Temperature | 320 - 330 | °C | |
Middle - Zone 2 Temperature | 310 - 320 | °C | |
Rear - Zone 1 Temperature | 295 - 305 | °C | |
Mold Temperature | 80 - 110 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 5 mm/min | 126 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 126 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | 2 | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 2 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 12080 | MPa | ASTM D638 |
Flexural Stress, brk, 1.3 mm/min, 50 mm span | 189 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 10010 | MPa | ASTM D790 |
Tensile Stress, yield, 5 mm/min | 125 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min | 125 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 1.5 | % | ISO 527 |
Tensile Strain, break, 5 mm/min | 1.6 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 13540 | MPa | ISO 527 |
Flexural Modulus, 2 mm/min | 9640 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.34 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.12 | % | ASTM D570 |
Mold Shrinkage, flow, 24 hrs | 0.12 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.49 | % | ASTM D955 |
Density | 1.34 | g/cm³ | ISO 1183 |
Moisture Absorption (23°C / 50% RH) | 0.16 | % | ISO 62 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 141 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 137 | °C | ASTM D648 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 145 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 140 | °C | ISO 75/Af |