LNP STAT-KON DJ000I is a compound based on PC resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1E03 - 1E07 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 660 | J/m | ASTM D256 |
| Izod Impact, notched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 137 | kJ/m² | ISO 180/1U |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time (Cumulative) | 2 | Hrs | |
| Rear - Zone 1 Temperature | 300 - 325 | °C | |
| Middle - Zone 2 Temperature | 310 - 335 | °C | |
| Front - Zone 3 Temperature | 315 - 340 | °C | |
| Melt Temperature | 310 - 335 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Screw Speed | 70 - 120 | rpm | |
| Injection Speed | 50 - 60 | mm/s | |
| Back Pressure | 0.5 - 5 | MPa |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 50 mm/min | 52 | MPa | ISO 527 |
| Tensile Strain, break, 50 mm/min | 15 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2510 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2460 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.2 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 300°C/5.0 kg | 22 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 126 | °C | ISO 75/Af |