LNP™ STAT-KON™ Compound DX02437

LNP STAT-KON DX02437 compound is based on Polycarbonate (PC) resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive, Impact Modified.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding
Extrusion

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Electrically Conductive
Impact resistant
No PFAS intentionally added

Industry

Material previously used in

Electronic Components
Material Handling

Applications

Possible usage of material

Electronic Components
Enclosures
LED Lighting
Semiconductor
carrier tape
electronic packaging
electronic handling

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	1.41E+07	Ω.cm	ASTM D257
Surface Resistivity	4.8E+07	Ω	ASTM D257

FILM EXTRUSION

PROPERTIES	TYPICAL VALUES	UNITS
Drying Time	4	Hrs
Drying Temperature	120 - 120	°C
Barrell Temperature - Rear	250 - 280	°C
Barrell Temperature - Middle	260 - 300	°C
Barrell Temperature - Front	260 - 300	°C
Roll Temperature	80 - 100	°C

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	2140	J/m	ASTM D4812
Izod Impact, notched, 23°C	359	J/m	ASTM D256
Izod Impact, notched, 0°C	294	J/m	ASTM D256
Instrumented Dart Impact Energy @ peak, 23°C	27	J	ASTM D3763
Multiaxial Impact	63	J	ISO 6603
Instrumented Dart Impact Total Energy, 23°C	39	J	ASTM D3763
*Izod Impact, unnotched 80104 +23°C*	130	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	24	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 0°C*	20	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	26	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	95	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	305 - 325	°C
Front - Zone 3 Temperature	320 - 330	°C
Middle - Zone 2 Temperature	310 - 320	°C
Rear - Zone 1 Temperature	295 - 305	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	58	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	47	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	19.3	%	ASTM D638
Tensile Modulus, 5 mm/min	2560	MPa	ASTM D638
Tensile Stress, yield, 5 mm/min	58	MPa	ISO 527
Tensile Stress, break, 5 mm/min	47	MPa	ISO 527
Tensile Strain, break, 5 mm/min	16.5	%	ISO 527
Tensile Modulus, 1 mm/min	2550	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	92	MPa	ISO 178
Flexural Stress, break, 2 mm/min	90	MPa	ISO 178
Flexural Strain, break, 2 mm/min	7.8	%	ISO 178
Flexural Modulus, 2 mm/min	2550	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.236	g/cm³	ASTM D792
Mold Shrinkage, flow, 1.5-3.2 mm	0.64	%	SABIC method
Mold Shrinkage, xflow, 1.5-3.2 mm	0.68	%	SABIC method
Melt Volume Rate, MVR at 300°C/5.0 kg	16	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Vicat Softening Temp, Rate A/50	144	°C	ASTM D1525
HDT, 1.82 MPa, 3.2 mm	111	°C	ASTM D648
Vicat Softening Temp, Rate A/50	144	°C	ISO 306
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	126	°C	ISO 75/Af

Register for High value Multi-Point Data