LNP™ STAT-KON™ Compound DX05042

LNP STAT-KON DX05042 compound is based on Polycarbonate (PC) resin containing 10% PTFE, 20% carbon fiber, 5% glass fiber. Added features of this grade include: Electrically Conductive, Wear Resistant, Easy Molding.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Carbon fiber filled
Electrically Conductive
Good Processability
High stiffness/Strength
Wear resistant

Industry

Material previously used in

Electronic Components
Material Handling

Applications

Possible usage of material

Electrical

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+02 - 1.E+03	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	11	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	45	kJ/m²	ISO 180/1U
Izod Impact, notched, 23°C	100	J/m	ASTM D256
Izod Impact, unnotched, 23°C	640	J/m	ASTM D4812
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	11	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	45	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	305 - 325	°C
Front - Zone 3 Temperature	320 - 330	°C
Middle - Zone 2 Temperature	310 - 320	°C
Rear - Zone 1 Temperature	295 - 305	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break, 5 mm/min	167	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.1	%	ISO 527
Tensile Modulus, 1 mm/min	16400	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	256	MPa	ISO 178
Flexural Modulus, 2 mm/min	14100	MPa	ISO 178
Tensile Stress, brk, Type I, 5 mm/min	169	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.4	%	ASTM D638
Tensile Modulus, 5 mm/min	16400	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	248	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	13100	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Mold Shrinkage, flow	0.2 - 0.4	%	SABIC method
Mold Shrinkage, xflow	0.4	%	SABIC method
Density	1.37	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.08	%	ISO 62
Moisture Absorption, (23°C/50% RH/24 hrs)	0.02	%	ASTM D570
Water Absorption, (23°C/24hrs)	0.15	%	ASTM D570
Water Absorption, (23°C/saturated)	0.27	%	ISO 62-1
Wear Factor Washer	36	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF	0.23	-	ASTM D3702 Modified: Manual
Static COF	0.39	-	ASTM D3702 Modified: Manual

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Vicat Softening Temp, Rate B/50	143	°C	ISO 306
Vicat Softening Temp, Rate B/50	143	°C	ASTM D1525
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	144	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	137	°C	ISO 75/Af
HDT, 1.82 MPa, 3.2mm, unannealed	135	°C	ASTM D648
CTE, 23°C to 80°C, flow	1.0E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	8.4E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, flow	0.8E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	7.5E-05	1/°C	ASTM E831

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES