ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.0E+06 - 1.0E+09 | Ω.cm | ASTM D257 |
Surface Resistivity | 1.0E+06 - 1.0E+09 | Ω | ASTM D257 |
LNP STAT-KON DX07323 compound is based on Polycarbonate (PC) resin containing stainless steel fiber. Added features of this grade include: Electrically Conductive, Impact Modified, meet ATEX requirements.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.0E+06 - 1.0E+09 | Ω.cm | ASTM D257 |
Surface Resistivity | 1.0E+06 - 1.0E+09 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-1 Flame Class Rating | 2.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 1600 | J/m | ASTM D4812 |
Izod Impact, unnotched, -40°C | 1500 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 180 | J/m | ASTM D256 |
Izod Impact, notched, -40°C | 100 | J/m | ASTM D256 |
Izod Impact, unnotched 80*10*4 +23°C | 130 | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*4 -40°C | 100 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 16 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -40°C | 10 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 48 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 295 - 315 | °C | |
Nozzle Temperature | 290 - 310 | °C | |
Front - Zone 3 Temperature | 295 - 315 | °C | |
Middle - Zone 2 Temperature | 280 - 305 | °C | |
Rear - Zone 1 Temperature | 270 - 295 | °C | |
Mold Temperature | 70 - 95 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 70 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield | 55 | MPa | ASTM D638 |
Tensile Stress, break | 45 | MPa | ASTM D638 |
Tensile Strain, yield | 5 | % | ASTM D638 |
Tensile Strain, break | 9 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 2400 | MPa | ASTM D638 |
Flexural Stress | 84 | MPa | ASTM D790 |
Flexural Modulus | 2200 | MPa | ASTM D790 |
Tensile Stress, yield, 5 mm/min | 55 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min | 44 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 5 | % | ISO 527 |
Tensile Strain, break, 5 mm/min | 9 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 |
Flexural Stress, break, 2 mm/min | 88 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2400 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.26 | g/cm³ | ASTM D792 |
Mold Shrinkage, flow | 0.5 | % | SABIC method |
Mold Shrinkage, xflow | 0.5 | % | SABIC method |
Mold Shrinkage, flow, 24 hrs | 0.4 - 0.7 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.4 - 0.7 | % | ASTM D955 |
Melt Flow Rate, 300°C/10 kgf | 55 | g/10 min | ASTM D1238 |
Density | 1.26 | g/cm³ | ISO 1183 |
Melt Volume Rate, MVR at 300°C/10.0 kg | 50 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 125 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 5.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 5.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 5.E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 124 | °C | ISO 75/Af |
Relative Temp Index, Elec | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |