LNP™ STAT-KON™ Compound DX96573C

LNP STAT-KON DX96573C compound is based on Polycarbonate (PC) resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive, LNP Clean Compounding Technology.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Electrically Conductive
Low ionics/Outgassing/Liquid particle count
No PFAS intentionally added

Industry

Material previously used in

Electrical
Electronic Components
Material Handling
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.0E+02 - 1.0E+05	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	65.8	J/m	ASTM D256
Izod Impact, unnotched, 23°C	NB	J/m	ASTM D4812
Instrumented Dart Impact Total Energy, 23°C	41	J	ASTM D3763
*Izod Impact, notched 80104 +23°C*	7.5	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	NB	kJ/m²	ISO 180/1U
Multiaxial Impact	38	J	ISO 6603

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	121	°C
Drying Time	4	Hrs
Melt Temperature	304 - 326	°C
Front - Zone 3 Temperature	321 - 332	°C
Middle - Zone 2 Temperature	310 - 321	°C
Rear - Zone 1 Temperature	293 - 304	°C
Mold Temperature	82 - 110	°C
Back Pressure	0.17 - 0.34	MPa
Screw Speed	30 - 60	rpm
Maximum Moisture Content	0.02	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 5 mm/min	3008	MPa	ASTM D638
Tensile Stress, yld, Type I, 5 mm/min	64	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	54	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	4.9	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	20	%	ASTM D638
Tensile Modulus, 1 mm/min	2913	MPa	ISO 527
Tensile Stress, yield, 5 mm/min	63	MPa	ISO 527
Tensile Stress, break, 5 mm/min	54	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	4.9	%	ISO 527
Tensile Strain, break, 5 mm/min	20	%	ISO 527
Flexural modulus	2890	MPa	ASTM D790
Flexural Modulus	2771	MPa	ISO 178
Flexural Stress	100	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.25	-	ASTM D792
Density	1.25	g/cm³	ASTM D792
Mold Shrinkage, flow, 24 hrs	0.74	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.85	%	ASTM D955
Moisture Absorption, (23°C/50% RH/24 hrs)	0.15	%	ASTM D570
Moisture Absorption (23°C / 50% RH)	0.23	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.8 MPa, 3.2mm, unannealed	133	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	142	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	131	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	142	°C	ISO 75/Bf
CTE, -30°C to 30°C, flow	0.000062	1/°C	ASTM E831
CTE, -30°C to 30°C, xflow	0.000063	1/°C	ASTM E831

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES