LNP STAT-KON EE004 compound is based on Polyetherimide (PEI) resin containing 20% carbon fiber. Added features of this grade include: Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.E+02 - 1.E+06 | Ω.cm | ASTM D257 |
Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 534 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 58 | J/m | ASTM D256 |
Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 150 | °C | |
Drying Time | 4 - 6 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 360 - 400 | °C | |
Rear - Zone 1 Temperature | 360 - 380 | °C | |
Middle - Zone 2 Temperature | 370 - 390 | °C | |
Front - Zone 3 Temperature | 380 - 400 | °C | |
Nozzle Temperature | 390 - 400 | °C | |
Mold Temperature | 140 - 180 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw speed (Circumferential speed) | 0.2 - 0.3 | m/s | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 170 | MPa | ASTM D638 |
Tensile Strain, break | 2 | % | ASTM D638 |
Flexural Stress | 259 | MPa | ASTM D790 |
Flexural Modulus | 12330 | MPa | ASTM D790 |
Tensile Modulus, 1 mm/min | 14800 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min | 195 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 1.7 | % | ISO 527 |
Flexural Modulus, 2 mm/min | 12300 | MPa | ISO 178 |
Flexural Strength, 2 mm/min | 264 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.34 | g/cm³ | ASTM D792 |
Mold Shrinkage, flow, 24 hrs | 0.1 - 0.3 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.3 - 0.5 | % | ASTM D955 |
Mold Shrinkage, flow, 24 hrs | 0.1 - 0.3 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 0.3 - 0.5 | % | ISO 294 |
Density | 1.34 | g/cm³ | ISO 1183 |
Moisture Absorption (23°C / 50% RH) | 0.2 | % | ISO 62 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 212 | °C | ASTM D648 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 212 | °C | ISO 75/Af |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 217 | °C | ISO 75/Bf |
CTE, -40°C to 40°C, flow | 1.E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, flow | 1.E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 4.7E-05 | 1/°C | ISO 11359-2 |
Relative Temp Index, Elec | 105 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 105 | °C | UL 746B |