LNP™ STAT-KON™ Compound EJ000C

LNP STAT-KON* EJ000C is a static dissipative compound based on Polyetherimide (PEI) resin containing carbon nanotubes. Added features of this grade include: LNP Clean Compounding Technology, Dimensional Stability. This material has a fit in broad range of markets including the semiconductor industry (e.g. HDD parts).

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyetherimide (PEI)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

No PFAS intentionally added
Thermally conductive/Electrically isolative

Industry

Material previously used in

Electronic Components
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Electronic Components
Semiconductor
blanks case
blanks
photomask
reticle
mask
foup
casette
stock shape
plate
bar

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1E+04 - 1E+07	Ω	ASTM D257
Surface Resistivity	1E+04 - 1E+07	Ω	ANSI/ESD STM11.11
Volume Resistivity	1E+00 - 1E+02	Ω.cm	SABIC method

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	5	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	52	kJ/m²	ISO 180/1U
Izod Impact, notched, 23°C	41	J/m	ASTM D256
Izod Impact, unnotched, 23°C	645	J/m	ASTM D4812

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	150	°C
Drying Time	4 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	340 - 400	°C
Rear - Zone 1 Temperature	340 - 380	°C
Middle - Zone 2 Temperature	350 - 390	°C
Front - Zone 3 Temperature	360 - 400	°C
Nozzle Temperature	390 - 400	°C
Mold Temperature	140 - 180	°C
Back Pressure	0.3 - 0.7	MPa
Screw speed (Circumferential speed)	0.15 - 0.2	m/s

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 1 mm/min	3650	MPa	ISO 527
Tensile Stress, break, 50 mm/min	110	MPa	ISO 527
Tensile Strain, break, 50 mm/min	4	%	ISO 527
Flexural Modulus, 2 mm/min	3620	MPa	ISO 178
Flexural Strength, 2 mm/min	172	MPa	ISO 178
Tensile Modulus, 50 mm/min	3780	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	110	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	4	%	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	3970	MPa	ASTM D790
Flexural Strength, 1.3 mm/min, 50 mm span	176	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Melt Volume Rate, MVR at 320°C/10.0 kg	3.6	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 340°C/5.0 kg	2.5	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 360°C/5.0 kg	5.8	cm³/10 min	ISO 1133
Mold Shrinkage, flow	0.5 - 0.7	%	SABIC method
Mold Shrinkage, xflow	0.5 - 0.7	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	201	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	211	°C	ISO 75/Bf
CTE, -40°C to 40°C, flow	4.0E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	4.0E-05	1/°C	ISO 11359-2
HDT, 1.82 MPa, 3.2mm, unannealed	201	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	211	°C	ASTM D648

CAE Cards

Please login to view graphs, download multi-point data or literature

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES