LNP™ STAT-KON™ Compound EJL20C

LNP STAT-KON EJL20C is a static dissipative and wear resistant compound based on Polyetherimide (PEI) resin containing carbon nanotubes and PTFE. Added features of this grade include: LNP Clean Compounding Technology, Dimensional Stability, Wear Resistance. This material has a fit in broad range of markets including the semiconductor industry.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyetherimide (PEI)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Dimensional stability
Electrically Conductive
Low ionics/Outgassing/Liquid particle count
Wear resistant

Industry

Material previously used in

Electrical
Electronic Components
Material Handling

Applications

Possible usage of material

Electronic Components

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+04 - 1.E+07	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	48	J/m	ASTM D256
Izod Impact, unnotched, 23°C	610	J/m	ASTM D4812
*Izod Impact, notched 80103 +23°C*	6	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80103 +23°C*	48	kJ/m²	ISO 180/1U

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	150	°C
Drying Time	4 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	340 - 400	°C
Nozzle Temperature	380 - 400	°C
Front - Zone 3 Temperature	360 - 400	°C
Middle - Zone 2 Temperature	350 - 390	°C
Rear - Zone 1 Temperature	340 - 380	°C
Mold Temperature	140 - 180	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	1.5 - 2	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 50 mm/min	98	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	5	%	ASTM D638
Tensile Modulus, 50 mm/min	2900	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	140	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	3100	MPa	ASTM D790
Tensile Stress, break, 50 mm/min	103	MPa	ISO 527
Tensile Strain, break, 50 mm/min	7	%	ISO 527
Tensile Modulus, 1 mm/min	3660	MPa	ISO 527
Flexural Strength, 2 mm/min	146	MPa	ISO 178
Flexural Modulus, 2 mm/min	3260	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.34	-	ASTM D792
Melt Volume Rate, MVR at 337°C/6.7 kg	3	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	210	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	200	°C	ASTM D648

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES